Date：2025-06-13 Views：1015
| C % | Ni % | Mo% | Cr% | P% | S% | V% | Fe % |
| 0.2 - 0.4 | 1.9 - 2.1 | 0.4 - 0.6 | 0.8 - 1.0 | ≦0.002 | ≦0.002 | Bal. |
| Parameter | Unit | Typical Value | Reference Range | Testing Method |
| Melt Index | g/10min | 200 | 150 - 300 | ISO 1133 (190 ℃, 21.6Kg) |
| Green Density | g/cm³ | 5.10 | 5.08 - 5.12 | ISO 3369 |
| Sintered Density | g/cm³ | 7.7 | 7.65 - 7.75 | ISO 3369 |
| Mold Factor | 1.190 | 1.185 - 1.195 | Mold Dimension / Product Dimension |
| Sintered State | Thermally Treated State | Thermally Treated State | |
| Density | ≥7.65g/cm³ | ||
| Yield Strength | ≥250MPa | ≥800 MPa | ≥1150 MPa |
| Tensile Strength | ≥350MPa | ≥900 MPa | ≥1300 MPa |
| Elongation | ≥5% | ≥3% | ≥2 % |
| Impact Value | ≥50J/m² | ||
| Hardness | 130 - 200 HV10 | ≥380 HV10（35 HRC） | ≥700 HV10（55 HRC） |
An advanced through - hardened versatile material. It's used in automotive parts, mechanical engineering, etc. Parts of this grade sintered in pure hydrogen can also be used as soft magnetic materials parts of similar grades.